Carbon Black, Furnace Black : We have available all types and qualities of prime Carbon Black, offgrade and scrap mixed qualities additives & filler for tires, plastics and rubbers, tonners chemical reagent, Batteries, refractories, various applications, as as well as in industrial rubber products, like belts, hoses and gaskets

Carbon Black
grade: N220, N330, N660, N550, M800


Carbon Black

- Mixed qualities production scrap
- The Cabon Black powder in from a dust
collector system.




gray spacergray spacer
CARBON BLACK PRIME QUALITIES, OFFGRADE AND
MIXED QUALITIES SCRAP.
 


 
    

Chemical and physical properties of carbon black
Grade ASTM test N-220 N-234 N-326 N-330 N-339 N-375 N-539 N-550 N-660
Iodine adsorp. No, g/kg D 1510 121ą5 120ą5 82ą5 82ą5 90ą5 90ą5 43ą5 43ą5 36ą5
DBP No, ml/100g D 2424 114ą5 125ą5 72ą5 102ą5 120ą5 1114ą5 111ą5 121ą5 90ą5
CTAB absorp. m2/kg D 3765 111ą5 119ą5 83ą5 82ą5 93ą5 96ą5 41ą5 42ą5 36ą5
Heating loss at 125 °C D 1509 1,0 max 1,0 max 1,0 max 1,0 max 1,0 max 1,0 max 1,0 max 1,0 max 1,0 max
Ash content % D 1506 max 1,0 max 1,0 max 1,0 max 1,0 max 1,0 max 1,0 max 1,0 max 1,0 max 1,0
Sieve resiude
N 35%
D 1514 0,001 max 0,001 max 0,001 max 0,001 max 0,001 max 0,001 max 0,001 max 0,001 max 0,001 max
Sieve resiude
N 325%
0,10 max 0,10 max 0,10 max 0,10 max 0,10 max 0,10 max 0,10 max 0,10 max 0,10 max
Fine Content % D 1508 max 7 max 7 max 6 max 7 max 7 max 7 max 7 max 7 max 7
pour density kg/m3 D 1513 345ą30 320ą30 465ą30 375ą30 345ą30 345ą30 385ą30 360ą30 425ą30
Sulphur content % D 1619 1,1 max 1,1 max 1,1 max 1,1 max 1,1 max 1,1 max 1,1 max 1,1 max 1,1 max
Colour strength % D 3265  115ą5 124ą5 112ą5 103ą5 110ą5 115ą5 - - -
DBP No, after pressing ml/100g D 3493 100ą5 103ą5 - 88ą5 101ą5 97ą5 84ą5 88ą5 75ą5
pH value D 1512 7-10 7-10 7-10 7-10 7-10 7-10 7-10 7-10 7-10
Toluol extract% D 1618 90 min 90 min 90 min 85 min 75 min 75 min 80 min 80 min 75 min
Pellet hardness g D 3303 15-100 15-100 15-100 15-100 15-100 15-100 15-100 15-100 15-100

Grade Description / Uses
N-234 Fine active carbon black with increased structure. Provides high wear resistance and high level of reinforcement of different rubbers. Rubbers, containing N-234, are characterized by high modulus and good smoth extrusion of raw compound. Car tyre treads with high performance, retreading. High quality industrial rubber goods and conveyor belts.
N-220 Fine active carbon black. Imparts to rubber high wear resistance and tear strength, relatively low modulus.
Tyre tread, retreading. High-quality industrial rubber goods and high grade conveyor belts.
N-375 Fine active carbon black. Provide high breaking and wear resistance. Improved ability of process. Tyre treads, retreading. Industrial rubber goods and conveyor belts.
N-339 Fine active carbon black with increased strucure. Imparts high modulus, improved extrusion, wear resistance and hysteresis N-330. Tyre treads, retreading. Industrial rubber goods and conveyor belts.
N-330  Fine active carbon black. Provides high stensile strength and good wear resistance. Tyre breaker and sidewalls. Solid tyres, agrucultural tyres, sleeve, conveyor belts, industrial rubber goods, fan-belt.
N-326 Fine low-structure active carbon black. Gives low modulus, high elongation at break, high tear and fatigue strength. Compundus for tyre breaker, including breaker for solid and off-road tyres.
N-550 Medium-dispersion, medium-active carbon black. Imparts high extrudability, relatively high tear resistance.
Compounds for tyre carcass and tube. Profile-extruded goods. Industrial rubber good, seal, hoses.
N-539 Similar to N-550 it is medium-dispersion, medium-active carbon black. Provides improved processing properties, possible increased loading. Compounds for tyre carcass and tube. Profile-extruded goods. Industrial rubber good, seal, hoses. One-layer roofing system.
N-660 Medium-dispersion, medium-active, low-structure carbon black. Provides higher die-swell, high resilience at relatively high hardness. May be incorporated in large quantity. Compounds for tyre carcass and tube. Moulded goods, goods extrusion. Industrial rubber goods, sleeves. One-layer roofing system. Isolating cable rubbers.
Chemical and physical properties of carbon black
Grade K-163 K-173 K-354 N-772 N-990 Test metode
Iodine No, mg/g - - 80±5 22-34 5-15 ASTM D-1510
DBP absorption, cm3/100g - - 95-110 70-80
or
65±5
 30-45
or
35±5
ASTM D-2414
pH of water suspension - - 3,7-4,7 9-11 7-11 ASTM D-1512
Fraction of total mass loss
at 105 °C %, max
6 5 1,5 0,5 0,15 ASTM D-1509
Ash content, max% 0,2 0,1 0,05 0,5 0,15 ASTM D-1506
Fraction of total mass loss after
screening through a mesh %, max
  ASTM D-1506
35 mm - - 0,001 0,001 0,001
325 mm - - 0,08 0,08 0,08
Dush content , max% - - 6 7 8 ASTM D-1508
Bulk density, kg/m3, min - - 340 420 330 ASTM D-1513
Specific surface, mg2/g min 190 min 230 90-100 33-39 12-16 GOST 7885-86
Average size of particles, mm 10-19 10-19 25-30 60-100 >200 Electron microscope
Grade Description Field of application Uses
N-990 This is obtained by thermal decomposition of natural gas in batch furnaces without access for air. It belongs to low active grades of carbon black and is characterized by the most low values of specific surface and structure index in comparison with other grades. It is made inpellet or powder form. For rubbers Ensures excellent technological properties of rubber mixes while processing, possibility to attain a high degree of filling of polymeric composition thus used for manufacturer of conveyor belts, as inactive filler for tyres, industrial rubber goods with a high content of the filler.
For carbon graphite materials It graphitizes well. Along with the strenghtening effect it ensures a high conductivity of articles. It shows a low gas emission during heat treatment. It gives good technological properties to mixes.
N-772 It is obtained in a continuous process in the furnace by a thermal-oxidative decomposition of natural gas. It belongs to semiactive grades of carbon black and it shows low values of dispersion and structural features. It is made in pellet form.  For rubbers Good dynamic properties to rubbers with a relatively low dispersion are imparted by this grade of carbon black. It allows to obtain an optimum combination processing of mixes. It is used in manufacture of frameworks, extruding rubber articles, tube, rubber articles subject to dynamic loads. It is also used as a semiactive filler in production of the industrial rubber articles, it is used in masterbatch.
For paintwork materials and for painting polymeric materials It is used to give a black tint in the mix for printing ink, as a pigment for plastic materials, UV - stabilizer for polyolefins. This grade of carbon black is one of major components of masterbatch which is used for pigmenting.
K-354 This is obtained by a channel mode in a diffusive flame during a thermal-oxidatative decomposition of natural gas. It belongs to active graded of carbon black and it has a high dispersion value and a low structural value. It is a highly dispersive and enhancing filler and a pigment. It is made in pellet form. For rubbers Makes rubber mixes resistant to premature vulcanization. Makes vulcanizate and articles strong when static and dynamic loads are applied. It is used for production of extra strong industrial rubber goods.
For paintwork materials,  painting of polymeric materials and for perfumery It disperses well and forms highly stable dispersions. It ensures an intensive black colour of materials, excellent apperance of coats, resistance of painting to the ultraviolet radiation. It is used for making intensively black varnishes and coast, synthetic fibres, printing ink, carbon paper, typewriter tapes, in perfumery for making the eyelash ink.
K-163
K-173-0
 The pigment carbon black is obtained by the channel method by setting carbon black particles which are performed in the diffusion flame with an incomplete combustion of natural gas, on a metal surface with a further oxidation (K-173-0) or without oxidation. These belong to special highly black grades of the carbon black and they are characterized by a high dispersion value and a high content of volatiles. For carbon graphite materials This gives a good enhancing effect due to a high dispersion ability and an active surface. It is highly pure from the point of view of content of mineral admixtures.
For paintwork materials,  painting of polymeric materials and for perfumery These are high quality ultra dispersing black pigments which ensure a high depth of black colour of the paintwork and impressions, resistance of the paint to the ultraviolet radiation, lustre of the nitrocellulose enamels for cars. These disperse well and highly stable dispersions are obtained as a result of this. They are used for making paints, varnishes, painting ink, rolling paste for printing arts, carbon paper for eyelash ink.